Terluran? HI-10
丙烯腈丁二烯苯乙烯
INEOS Styrolution Group GmbH
产品说明:
Terluran? HI-10 is an medium flow, injection molding grade with very high resistance to impact with excellent heat distortion and suitable for injection molding and extrusion.
FEATURES
APPLICATIONS
特性 | - 超高抗攻击性、刚性，高、高强度、流动性中等、耐低温、攻击韧性良好
|
用途 | |
形式 | |
加工要领 | |
多点数据 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
|
密度 / 比重 |
|
|
|
-- | 1.03 |
| ASTM D792 |
-- | 1.03 | g/cm? | ISO 1183 |
熔流率（熔体流动速率） |
|
| ASTM D1238 |
200°C/5.0 kg | 0.10 | g/10 min |
|
220°C/10.0 kg | 8.0 | g/10 min |
|
溶化体积流率（MVR） |
|
|
|
230°C/3.8 kg | 0.104 | in?/10min | ASTM D1238 |
220°C/10.0 kg | 0.336 | in?/10min | ISO 1133 |
收缩率 |
|
|
|
流动 | 4.0E-3 到 7.0E-3 | in/in | ASTM D955 |
-- | 0.40 到 0.70 | % | ISO 294-4 |
吸水率 |
|
|
|
饱和, 73°F | 1.0 | % | ASTM D570, ISO 62 |
平衡, 73°F, 50% RH | 0.21 | % | ISO 62 |
洛氏硬度 (R 级) | 95 |
| ASTM D785 |
球压硬度 | 10700 | psi | ISO 2039-1 |
拉伸模量 |
|
|
|
-- | 290000 | psi | ASTM D638 |
-- | 276000 | psi | ISO 527-2 |
抗张强度 |
|
|
|
屈服, 73°F | 6240 | psi | ASTM D638 |
屈服, 73°F | 5510 | psi | ISO 527-2 |
拉伸应变 |
|
|
|
屈服, 73°F | 2.8 | % | ISO 527-2 |
断裂 | 3.5 | % | ASTM D638 |
标称拉伸断裂应变 (73°F) | 9.0 | % | ISO 527-2 |
弯曲模量 | 297000 | psi | ASTM D790 |
弯曲强度 |
|
|
|
-- | 9570 | psi | ASTM D790 |
-- | 8120 | psi | ISO 178 |
简支梁缺口攻击强度 |
|
| ISO 179 |
-22°F | 6.2 | ft·lb/in? |
|
73°F | 17 | ft·lb/in? |
|
简支梁无缺口攻击强度 |
|
| ISO 179 |
-22°F | 67 | ft·lb/in? |
|
73°F | 无断裂 |
|
|
悬壁梁缺口攻击强度 |
|
|
|
-22°F | 2.2 | ft·lb/in | ASTM D256 |
0°F | 3.4 | ft·lb/in | ASTM D256 |
73°F | 8.4 | ft·lb/in | ASTM D256 |
-22°F | 6.7 | ft·lb/in? | ISO 180/A |
73°F | 17 | ft·lb/in? | ISO 180/A |
载荷下热变形温度 |
|
|
|
66 psi, 未退火 | 201 | °F | ASTM D648 |
66 psi, 退火 | 215 | °F | ASTM D648 |
66 psi, 退火 3 | 207 | °F | ISO 75-2/B |
264 psi, 未退火 | 186 | °F | ASTM D648 |
264 psi, 退火 | 208 | °F | ASTM D648 |
264 psi, 退火 3 | 199 | °F | ISO 75-2/A |
维卡软化温度 |
|
|
|
-- | 217 | °F | ISO 306/A50 |
-- | 194 | °F | ISO 306/B50 |
线形热膨胀系数 - 流动 | 4.4E-5 到 6.1E-5 | in/in/°F | ISO 11359-2 |
导热系数 | 1.2 | Btu·in/hr/ft?/°F | DIN 52612 |
体积电阻率 |
|
|
|
-- | > 1.0E+15 | ohms·cm | ASTM D257 |
-- | 1.0E+15 | ohms·cm | IEC 60093 |
介电常数 |
|
|
|
0.0394 in, 1 MHz | 2.80 |
| ASTM D150 |
100 Hz | 2.90 |
| IEC 60250 |
1 MHz | 2.80 |
| IEC 60250 |
耗散因数 |
|
| IEC 60250 |
100 Hz | 5.4E-3 |
|
|
1 MHz | 8.2E-3 |
|
|
干燥温度 | 176 | °F |
|
干燥时间 | 2.0 到 4.0 | hr |
|
加工（熔体）温度 | 446 到 500 | °F |
|
模具温度 | 86 到 176 | °F |
|
Injection Velocity | 472 | in/min |
|
如需苯领原厂物性表及相关文件，请联系腾博会官网事情人员，谢谢！